Application of Zinc Methacrylate in Chlorinated Polyethylene / Ethylene-Propylene-Diene Rubber Insulation
-
摘要: 为提升氯化聚乙烯(CM)/三元乙丙橡胶(EPDM)共混绝缘胶料(简称绝缘胶料)的性能,研究了甲基丙烯酸锌(ZDMA)添加方式与用量、过氧化物用量等对绝缘胶料硫化特性、加工性能和物理机械性能的影响。结果表明,在过氧化二异丙苯硫化体系中,ZDMA相较于常用的交联助剂,具有更高的硫化效率,对绝缘胶料机械性能的影响较大。当ZDMA用量为4份且氧化锌(ZnO)/甲基丙烯酸(MMA)的摩尔比为0.8时,原位生成法合成的绝缘胶料物理机械性能和加工性能最佳;当ZDMA用量超过5份时,绝缘胶料容易出现粘模现象,影响加工性能。文中研究可为高性能绝缘电缆胶料的生产制备提供参考。
-
关键词:
- 甲基丙烯酸锌 /
- 原位合成 /
- 氯化聚乙烯/三元乙丙橡胶绝缘胶料 /
- 物理机械性能
Abstract: To enhance performance of chlorinated polyethylene (CM)/ethylene-propylene-diene rubber (EPDM) blend insulating compounds (a bbreviated as insulating compounds),the effects of addition method and dosage of zinc methacrylate (ZDMA),amount of peroxide,on vulcanization characteristics,processing performance,and physical mechanical properties of insulating compounds were investigated.Results showed that in dicumyl peroxide vulcanization system,ZDMA had a higher vulcanization efficiency compared to commonly used crosslinking agents and had a significant impact on mechanical properties of vulcanized rubber.When the dosage of ZDMA was 4 parts and the molar ratio of zinc oxide (ZnO) to methyl methacrylate (MMA) was 0.8,physical mechanical properties and processing performance of in-situ synthesized insulating compounds were optimal;when the dosage of ZDMA exceeds 5 parts,insulating compounds were prone to mold sticking,affecting processing performance.The research could provide reference for production and preparation of high-performance insulating cable compounds. -
-
[1] 赵阳,张立群,卢咏来,等.不饱和羧酸金属盐在橡胶工业中的应用[J].橡胶工业,2000(8):497-502. [2] 何平,彭宗林,任文坛,等.原位合成甲基丙烯酸锌改性三元乙丙橡胶/聚丙烯热塑性弹性体[J].合成橡胶工业,2006(6):435-438. [3] 栗敬君,王同海,王海威,等.Zn(MMA)2对硫黄硫化天然橡胶性能的影响[J].当代化工,2017,46(3):404-408. [4] 彭宗林,梁讯,张勇,等.原位生成甲基丙烯酸盐对EPDM的增强(英文)[J].合成橡胶工业,2001(2):110. [5] 郭尚振,庄涛,时金凤,等.氧化锌/甲基丙烯酸对原位合成甲基丙烯酸锌增强三元乙丙橡胶性能的影响[J].合成橡胶工业,2016,39(6):499-503. [6] 虞宇力,彭宗林,张隐西,等.甲基丙烯酸锌对EPDM的补强作用[J].橡胶工业,2001(9):522-525. [7] 陈朝晖,王迪珍,罗东山,等.NBR/Zn(MAA)2合金性能与结构的关系[J].合成橡胶工业,2000(2):107-110. [8] 王增林,李再峰,孙宝全,等.甲基丙烯酸锌/炭黑增强氢化丁腈橡胶的性能[J].合成橡胶工业,2011,34(3):218-222. [9] 武守鹏,王增林,田帅承,等.甲基丙烯酸锌增强氢化丁腈橡胶复合材料的性能[J].合成橡胶工业,2014,37(5):376-379. [10] 姚亮,丛后罗,王国志,等.甲基丙烯酸盐对NBR/WRP复合材料性能的影响[J].橡塑技术与装备,2016,42(15):57-60. [11] 赵阳,卢咏来,刘力,等.甲基丙烯酸锌/丁腈橡胶纳米-微米混杂复合材料Ⅱ.微观结构与宏观性能[J].合成橡胶工业,2002(1):35-38. [12] 陈旭明,郭建华,何邦柳,等.甲基丙烯酸锌用量对天然橡胶高温蠕变性能的影响及数值模拟[J].高分子材料科学与工程,2019,35(7):147-151. [13] 曹杨,张景林,顾宁,等.甲基丙烯酸锌与蒙脱土补强天然橡胶的研究[J].中北大学学报(自然科学版),2011,32(3):314-317. [14] 王聿衡,彭宗林,张勇,等.原位合成甲基丙烯酸锌增强氢化丁腈橡胶[J].合成橡胶工业,2005(3):205-210. [15] 陈玉坤,贾德民,王小萍,等.原位生成甲基丙烯酸锌对天然橡胶补强的研究[J].现代化工,2005(4):39-42.
©上海电缆研究所有限公司《电线电缆》编辑部版权所有，未经授权不得转载、改编。
计量
- 文章访问数: 44
- HTML全文浏览量: 8
- PDF下载量: 34
下载: